Epoxy Resin from Transparent Stream for Table River Kit 5 kg - Up to 50 mm

• Resin composition - Epoxy polyetheramine
• Composition solvents - Alcohols (traces)
• Color - Colorless, transparent
• Degree of brightness at 60oC - >93 gloss
• Dosage - By weight: 3 parts component A, 1 part component B
• Pot life - 150 min. for 200g of mixing (A-B) at 25oC
• Application conditions - Ambient humidity: 50% maximum // Ambient temperature, support/painting: minimum 18oC
• Polymerization/Drying - At room temperature, by chemical reaction
• Dilution - Not necessary
• Removal time (50 mm thickness) - 48 hours at 20oC // 24 hours of rest at room temperature - 12 hours at 40oC
• Dry at heart at 20oC - 48 hours // Complete drying after 15 days
• Dry extract - 97% (by volume) // 99% (by weight)
• Density - 1.08 ±15 g/litre at 20oC
• Brookfield Viscosity - 200 cps (A-B) at 20oC 4/50 tpm
• Theoretical yield - 11 kg/m2 to 10 mm thick
• Flashpoint - >61oC
• Preservation - 12 months minimum in its original unseeded packaging, in a dry and cool place.
• Tool cleaning - Acetone

Mix the two components perfectly with a spatula, as indicated, scraping the sides and bottom of the container.

Council :

• to avoid mixing problems, you can pour this mixture into a new container and continue mixing for at least 3 minutes. Leave to rest for a few minutes before pouring the product, so that the air incorporated during the mixture can escape.

• To promote the mooring and removal of the microfoam, we advise you to apply a layer of the mixture on the walls of the mold and on the objects to be included before making the casting.

This product is formulated with low reactivity, so drying will be slow. However, it can be accelerated by allowing the drying to take place at a temperature of 40oC.

This low reactivity allows thicknesses greater than 50 mm to flow, avoiding any incorporation of air and a strong thermal reaction.

This resin can be tinted with epoxy dye paste and/or inert additives (aluminum, photoluminescent or pearly pigments) to create special effects.