Yachtcare Uniflex MS Polymer - 310 ml - White or Black

Collage and elastic sealing

Description

Single-component, solvent-free MS-Polymer mastic for a wide range of applications.

Very good grip on many mineral supports such as glass and metals. Does not contain isocyanates or halogens.

Good grip on wood and its derivatives as well as on many duroplast and thermoplastic materials (except TPEs).

Good resistance to humidity as well as to the usual climatic constraints.

APPLICATION AREAS

Single-component, high-mechanically performance putty, specially designed for flexible bonding and waterproofing of various materials such as polyester, metals (aluminium, stainless steel, zing, pre-laquered, etc.), wood and derivatives, glass, as well as many duroplast and thermoplastic materials (excluding PE, PP, PTFE).

The primary applications of this putty are in the industrial and refrigeration body, sandwich panels, air conditioning, shipyards and in many areas of the industry in general.

Elastic and very resistant, well-maintained at humidity and temperature from -40 to 80 degrees Celsius continuously, 120 degrees Celsius at peak.

Fresh cords can be painted in the first few hours after application (After skin formation, adhesion problems may appear with certain types of paints).

Virtually non-yellowing mastic during Ultra Violet radiation exposures. A formula free of halogens and isocyanates, which is particularly beneficial from an ecological and toxicological point of view.

Odorless product.

Technical

Base: Polyoxypropylene polymers polymerizing with air moisture

Consistency: Excellent thixotropy and great extrusion facility

Polymerization speed: 3 mm (on the first day) DIN 50 014 - 23oC/50% HR Skin training: 25 min. DIN 50,014 - 23oC/50% Hr

Traction resistance: 3.0 N/mm2 DIN 53,504 - NSt. S3A

Tear resistance: 20 N/mm ASTM D 624, Form B

310 ml cartridge

Available in black and white.